PRESENTASE KANDUNGAN MINYAK HASIL PENYULINGAN LDPE TERHADAP KARAKTERISTIKNYA

Saifudin Asngari, Muh Malyadi, Wawan Trisnadi Putra

Abstract


Plastic oil is a fuel produced from plastic, which is processed by means of distillation. In the plastic distillation process used LDPE (Low density polyethylene) plastic bag, this type of plastic is ductile and flexible in addition to this type of plastic also has a transparent nature, and is resistant in shock so that this type of plastic is widely used by the community for plastic wrapping. LDPE plastic is included in the type of thermoplastic is one of a group of plastics that are able to be recycled again so that it is easy in the distillation process. The results of diesel oil plastic types will be mixed with bio diesel and tested for density, color, distillation, flash point, sulfur content and cetane number values. In a mixture of 30% LDPE plastic type diesel oil and 70% bio diesel with a density of 843.3 kg / m3, has a clear and bright color, in the distillation process in a mixture of 30% LDPE plastic type diesel oil 70% bio diesel is known at initial temperatures IBP 150oC at 10% drop at 201oC at 50% drop at 289oC and at the last drop 90% at 347oC. a mixture of 30% LDPE plastic type diesel oil and 70% bio diesel has a flash pont value with 57oC test results. sulfur content in a mixture of 30% LDPE plastic type diesel oil and 70% bio diesel with a value of 0.11% m / m, in a mixture of 30% LDPE plastic type diesel oil and 70% bio diesel has a cetane number value of 53oC.


Keywords


Solar Type Plastic Oil, Bio Solar, Cetane Number

References


Adityo. (Agustus 2016). Nilai Kalor Campuran Premium Dengan Bahan Bakar Polypropilene Hasil Proses Pirolisis. Jurnal Ilmiah, 28.

Aladin, A. (Mei-2018). Potensi Pengolahan Limbah Plastik Kemasan Air Mineral Dengan Metode Pirolisis Menjadi Minyak Bahan Bakar Alternatif. Jurusan Teknik Kimia, Vol.03, No.01.

Dharma, U. S. (n.d.). Analisa Karakteristik Minyak Plastik Hasil Dua Kali Proses Pirolisis. Teknik mesin, no.4.

Ginting, I. S. (Desember 2017). Pengolahan Sampah Plastik Jenis Pp (Polypropylene) Sebagai. e-Proceeding of Art & Design, Vol.4,

No.3.

Iswadi, D., & dkk. (Juli, 2017).

Pemanfaatan Sampah Plastik Ldpe Dan Pet Menjadi Bahan Bakar Minyak Dengan Proses Pirolisis. Jurnal Ilmiah Teknik Kimia Unpam, No. 2 .

K, E., & dkk. (17 Maret 2016). Pengolahan Sampah Plastik dengan Metoda Pirolisis menjadi Bahan Bakar Minyak. Jurusan Teknik Kimia, no.1.

Landi, T. (2017). Perancangan Dan Uji Alat Pengolah Sampah Plastik Jenis Ldpe (Low Density Polyethylene) Menjadi Bahan Bakar Alternatif. Jurnal Teknik Mesin, Vol. 5, No. 1.

Liestiono, R. P., (2017). Karakteristik Minyak Dan Gas Hasil Proses Dekomposisi Termal Plastik Jenis Low Density Polyethylene (Ldpe). Jurnal Offshore, No. 2 .

Mafruddin, (2017). Pengaruh Geometri Pipa Kondensor Terhadap Perpindahan Panas Pada Destilasi Minyak Plastik. Jurnal Teknik Mesin Univ. Muhammadiyah Metro, Vol. 6 No. 2.

Manurung, N. (Tahun 2017). Pembuatan Bahan Bakar Minyak Dari Limbah Plastik Dengan Menggunakan Dua Kondensor. Jitekh, 11-16.

Mokhtar, A. (2018). Perancangan Pirolisis Untuk Membuat Bahan Bakar Cair Dari Limbah Plastik Kapasitas 10 Kg. Teknik Mesin, Universitas Muhammadiyah Malang, 128.

Muchammad. (April 2018). Analisis Pemanfaatan Limbah Sampah Plastik Jenis Polypropylene Menjadi Bahan Bakar Alternatif. Teknik Mesin, Fakultas Teknik, No. 1

Mujiarto, I. (Desember 2005). Sifat Dan Karakteristik Material Plastik Dan

Bahan Aditif . Staf Pengajar Amni

Semarang, No. 2.

Nasrun, & dkk. (2016). Studi Awal

Produksi Bahan Bakar Dari Proses Pirolisis Kantong Plastik Bekas. Jurnal Teknologi Kimia, 30-44.

Rekathakusuma, I. (December 2016). Karakterisasi Bahan Cair Produk Distilasi Sampah Plastik Dan Pemanfaatannya Sebagai Bahan Bakar. Teknik Fisika Fakultas Teknik, No.3 .

sari, G. l. (2017). Kajian Potensi Pemanfaatan Sampah Plastik Menjadi Bahan Bakar Cair. Jurnal Teknik Lingkungan, vol.3 no.1.

Siti Naimah, S. A. (19 September 2016). Karakteristik Pelarut Dan Solar Hasil Proses Pirolisis Limbah Plastik Polietilen. Balai Besar Kimia dan Kemasan, Kementerian Perindustrian, 38.

Surono, U. B. (2013). Berbagai Metode Konversi Sampah Plastik Menjadi Bahan Bakar Minyak. Jurnal Teknik, 25.


Full Text: PDF

DOI: 10.24269/jkt.v3i2.255

DOI (PDF): http://dx.doi.org/10.24269/jkt.v3i2.255.g241

Refbacks

  • There are currently no refbacks.